Pressure Sensitive Label Facestock Film Metalized, Top Coated on Metalized Side (UPAi)
C1023(MO) UPAi
Structure
Untreated HS layer
OPP core
Print receptive coated metallised layer
Description
Bi-axially Oriented Polypropylene metallised film, print receptive coated on metallised side.
Features
- Sparkling metallic appearance
- Coated print surface for excellent ink adhesion and high speed press performance
- Wide compatibility with ink systems (water based, UV & solvent based )
- Spectacular print performance across wide variety of printing process
- (flexography, gravure, silkscreen and hot or cold foiling etc.)
- High stiffness for conversion and dispensing
- Excellent moisture resistance
Applications
- Pressure sensitive labeling
Typical values
| Properties | Ref. | Units | ASTM#/ Test Method | C1023(MO) UPAi |
|---|
| Physical Data | |||||
| Average Thickness | Micron | D-374-C | 47 | 51 | |
| Gauge | 188 | 204 | |||
| Mils | 1.8 | 2.0 | |||
| Thickness Variation | %(±) | 3 | |||
| Average substance | g/m² | 42.23 | 45.8 | ||
| Yield | m²/Kg | D-4321 | 23.67 | 21.8 | |
| in²/lb | 16641 | 15326 | |||
| Optical Data | |||||
| Optical Density | CTM | 2.0 - 2.4 | |||
| Mechanical Data | |||||
| Tensile Strength | MD | kg/cm² | D-882 | 1100 - 1400 | |
| TD | 2400 - 2800 | ||||
| Elongation | MD | % | D-882 | 140 -200 | |
| TD | 30-80 | ||||
| Thermal Data | |||||
| Shrinkage (120⁰C/248 ⁰F,5 min) | MD | % | D-1204 | 2.0 - 4.0 | |
| TD | 0.5 - 2.0 | ||||
| CTM : Cosmo Test Method | MD : Machine Direction | TD : Transverse Direction |
| Disclaimer : The information provided above is based on COSMO FILMS LTD's conclusive tests, which are indicative only and provided as guidelines.They do not constitute a guarantee of any specific product attributes or the suitability of products for specific applications | ||
| Storage condition : Storage temperature to be maintained 25 Deg.C (+/-5 Deg C) & relative humidity 55% (+/-5%) to avoid accelerated reduction of surface treatment level. | ||
| Note : Corona treatment required before adhesive application on non coated side. | ||
Updation Date : 2023-Jul-13