Pressure Sensitive Label Facestock Film Metallised,Coated on Both Side
C1024(UPAi-UP) MO
Structure
Print receptive coated layer
OPP core
Adhesive receptive metallised coated layer
Description
It is co-extruded,one side coated for print receptivity and other side primer coated metallised Bi-axially oriented polypropylene film
Features
- Sparkling metallic appearance
- Coated print surface for excellent ink adhesion and high speed press performance
- Wide compatibility with ink system(UV, water based etc.)
- Spectacular print performance across wide variety of printing process(flexography,UV offset,TT printing,silkscreen,letter press Foiling etc.)
- High stiffness for conversion and dispensing
- Superior performance of print surface in humid enviornment
Applications
- Film suitable for label stock conversions
- After conversion used for pressure sensitive labels for beverages,health and beauty and pharmaceutical application
Typical values
| Properties | Ref. | Units | ASTM#/ Test Method | C1024(UPAi-UP) MO |
|---|
| Physical Data | ||||
| Average Thickness | Micron | D-374-C | 52 | |
| Gauge | 208 | |||
| mils | 2.0 | |||
| Thickness Variation | %(±) | 3 | ||
| Average substance | g/m² | 46.4 | ||
| Yield | m²/kg | D-4321 | 21.5 | |
| in²/lb | 15116 | |||
| Optical Data | ||||
| Optical Density | CTM | 2.0-2.4 | ||
| Mechanical Data | ||||
| Tensile Strength | MD | D-882 | 1100-1400 | |
| TD | 2400-2800 | |||
| Elongation | MD | % | D-882 | 140-200 |
| TD | 30-80 | |||
| Thermal Data | ||||
| Shrinkage (120⁰C/248 ⁰F,5 min) | MD | % | D-1204 | 2.0-4.0 |
| TD | 0.5-2.0 | |||
| CTM : Cosmo Test Method | MD : Machine Direction | TD : Transverse Direction |
| Disclaimer : The information provided above is based on COSMO FILMS LTD's conclusive tests, which are indicative only and provided as guidelines. They do not constitute a guarantee of any specific product attributes or the suitability of products for specific applications. | ||
| Storage condition : Storage temperature to be maintained 25 Deg.C (+/-5 Deg C) & relative humidity 55% (+/-5%) to avoid accelerated reduction of surface treatment level. | ||
| Note : Treatment values in metalized films tend to decay over a period of time during transportation & subjected to storage conditions, hence it is recommended to check the treatment prior to processing & if reduction is observed then go for online treatment, high adhesive GSM & a suitable primer may be applied. | ||