Pressure Sensitive Label Facestock Film White Opaque PET, Top Coated (PR)
C2005 (PR) HO
Structure
Coated print receptive layer
White PET core
Corona treated layer
Description
A superb white opaque PET film with one side print receptive coating and other side corona treated surface.
Features
- Superb whiteness and high opacity
- Wide compatibility with ink system (UV, water based etc.)
- Print receptive coated surface for excellent ink adhesion and high speed press performance
- Spectacular print performance across wide variety of printing process
- (flexography, UV offset, TT Printing, silkscreen, Letter press, Foiling etc.)
- Corona treated surface suitable for adhesive receptivity
- High stiffness for conversion and dispensing
Applications
- Pressure sensitive labeling
Typical values
| Properties | Ref. | Units | ASTM#/ Test Method | C2005 (PR) HO |
|---|
| Physical Data | |||||
| Average Thickness | Micron | D-374-C | 46 | 51 | |
| Gauge | 184 | 204 | |||
| Mils | 1.8 | 2.0 | |||
| Thickness Variation | %(±) | 5 | |||
| Average substance | g/m² | 65.85 | 73.1 | ||
| Surface Tension(min) | SM Side | dynes/cm | D-2578 | 38 | |
| Yield | m²/Kg | D-4321 | 15.18 | 13.67 | |
| in²/lb | 10672 | 9611 | |||
| Optical Data | |||||
| Gloss (45⁰) | Gardner | D-2457 | >58 | ||
| Opacity | % | Hunter Lab D25-2CR | >83 | ||
| Whiteness Index | % | E-313 | >85 | ||
| Mechanical Data | |||||
| Tensile Strength | MD | kg/cm² | D-882 | 1200-1500 | |
| TD | 1400-1800 | ||||
| Elongation | MD | % | D-882 | 140 - 200 | |
| TD | 50-100 | ||||
| Thermal Data | |||||
| Shrinkage (120⁰C/248 ⁰F,5 min) | MD | % | D-1204 | 1.0 - 2.0 | |
| TD | 0.0 - 0.5 | ||||
| CTM : Cosmo Test Method | MD : Machine Direction | TD : Transverse Direction | CS: coated side |
| Disclaimer : The information provided above is based on COSMO FILMS LTD's conclusive tests, which are indicative only and provided as guidelines.They do not constitute a guarantee of any specific product attributes or the suitability of products for specific applications | |||