Label Film In- Mould Label, White
HST-2(IML) LB85
Structure
Treated, gloss printable OPP layer
Inter layer
Cavitated white pigmented OPP core
Inter layer
Treated matte OPP layer
Description
It is a co-extruded, one side glossy, other side matte and both sides corona treated white opaque Bi-axially Oriented Polypropylene film.
Features
- High yield
- Excellent machinability
- Printable surface with sparkling gloss
- Matte surface suitable for fusion with PP container
- High opacity & whiteness index
- Good antistatic
- Suitable for Offset, Rotogravure & Flexography printing.
Applications
- In-mold labels for PP & PE Injection molding
Typical values
| Properties | Ref. | Units | ASTM#/ Test Method | HST-2(IML) LB85 |
|---|
| Physical Data | |||||
| Average Thickness | Micron | D-374-C | 60 | 70 | |
| Gauge | 240 | 280 | |||
| Mils | 2.4 | 2.8 | |||
| Thickness Variation | %(±) | 5 | |||
| Density | g/cc | 0.85 | |||
| Average substance | g/m² | 51 | 59.5 | ||
| Surface Tension(min) | Both Side | dynes/cm | D-2578 | 38 | |
| Kinetic COF | M-M | D-1894 | 0.25-0.35 | ||
| Yield | m²/Kg | D-4321 | 19.6 | 16.8 | |
| in²/lb | 13780 | 11811 | |||
| Optical Data | |||||
| Gloss (45⁰) | Glossy Side | Gardner | D-2457 | 50-60 | |
| Opacity | % | Hunter Lab D25-2CR | >85 | ||
| Whiteness Index | % | E-313 | >90 | ||
| Mechanical Data | |||||
| Tensile Strength | MD | kg/cm² | D-882 | 800-1100 | |
| TD | 1800-2100 | ||||
| Elongation | MD | % | D-882 | 150-200 | |
| TD | 30-80 | ||||
| Thermal Data | |||||
| Shrinkage (120⁰C/248 ⁰F,5 min) | MD | % | D-1204 | 2.0-4.0 | |
| TD | 1.0-2.0 | ||||
| CTM : Cosmo Test Method | MD : Machine Direction | TD : Transverse Direction | M : Matte side |
| Disclaimer : The information provided above is based on COSMO FILMS LTD's conclusive tests, which are indicative only and provided as guidelines.They do not constitute a guarantee of any specific product attributes or the suitability of products for specific applications | |||
| Storage condition : Storage temperature to be maintained 25 Deg.C (+/-5 Deg C) & relative humidity 55% (+/-5%) to avoid accelerated reduction of surface treatment level. | |||
Updation Date : 2022-Aug-25