Pressure Sensitive Label Facestock Film Metallised, Non Coated
HST-2(MO) LBS
Structure
Aluminium layer
Modified treated, OPP layer
OPP core
Treated, HS OPP layer
Description
It is a co-extruded, one side metallised and other side treated heat sealable Bi-axially Oriented Polypropylene film.
Features
- Outstanding metal appearance
- Excellent metal adhesion to film
- Very Good barrier to moisture and light
- Good gas barrier
- High heat seal strength
- Very good printability
- Very good optics
- Good stiffness
Applications
- Self adhesive labels
Typical values
| Properties | Ref. | Units | ASTM#/ Test Method | HST-2(MO) LBS |
|---|
| Physical Data | ||||||
| Average Thickness | Micron | D-374-C | 40 | 46 | 50 | |
| Gauge | 160 | 184 | 200 | |||
| Mils | 1.6 | 1.8 | 2.0 | |||
| Thickness Variation | %(±) | 3 | ||||
| Density | g/cc | 0.905 | ||||
| Average substance | g/m² | 36.2 | 41.6 | 45.2 | ||
| Kinetic COF | NM-NM | D-1894 | 0.30-0.40 | |||
| Yield | m²/Kg | D-4321 | 27.62 | 24.0 | 22.1 | |
| in²/lb | 19418 | 16887 | 15537 | |||
| Optical Data | ||||||
| Optical Density | CTM | 2.0-2.4 | ||||
| Mechanical Data | ||||||
| Tensile Strength | MD | kg/cm² | D-882 | 1100-1400 | ||
| TD | 2400-2800 | |||||
| Elongation | MD | % | D-882 | 140-200 | ||
| TD | 30-70 | |||||
| Thermal Data | ||||||
| Shrinkage (120⁰C/248 ⁰F,5 min) | MD | % | D-1204 | 2.0-4.0 | ||
| TD | 0.5-2.5 | |||||
| CTM : Cosmo Test Method | MD : Machine Direction | TD : Transverse Direction | NM: Non - Metallised |
| Disclaimer : The information provided above is based on COSMO FILMS LTD's conclusive tests, which are indicative only and provided as guidelines.They do not constitute a guarantee of any specific product attributes or the suitability of products for specific applications | |||
| Storage condition : Storage temperature to be maintained 25 Deg.C (+/-5 Deg C) & relative humidity 55% (+/-5%) to avoid accelerated reduction of surface treatment level. | |||
| Note : Treatment values in metalized films tend to decay over a period of time during transportation & subjected to storage conditions, hence it is recommended to check the treatment prior to processing & if reduction is observed then go for online treatment, high adhesive GSM & a suitable primer may be applied. | |||