Plain Printing & Lamination Film
PCT-1(CV) HR
Structure
Hot slip modified OPP layer
Additive modified OPP core
Treated, printable OPP layer
Description
It is a co-extruded, plain, one side treated and out side hot slip modified Bi-axially Oriented Polypropylene film.
Features
- Excellent printability at high speed
- Excellent hot slip
- High heat resistance (up to 160°C*)
- Good ink adhesion
- Controlled COF up to 50°C
- Good antistatic
Applications
- Used as a reverse printed top layer into multilayer laminate
Typical values
| Properties | Ref. | Units | ASTM#/ Test Method | PCT-1(CV) HR |
|---|
| Physical Data | ||||||
| Average Thickness | Micron | D-374-C | 15 | 18 | 20 | |
| Gauge | 60 | 72 | 80 | |||
| Mils | 0.6 | 0.7 | 0.8 | |||
| Thickness Variation | %(±) | 3 | ||||
| Density | g/cc | 0.905 | ||||
| Average substance | g/m² | 13.58 | 16.29 | 18.1 | ||
| Surface Tension(min) | dynes/cm | D-2578 | 38 | |||
| Kinetic COF | UT-UT | D-1894 | 0.15-0.25 | |||
| Yield | m²/Kg | D-4321 | 73.6 | 61.4 | 55.2 | |
| in²/lb | 51772 | 43160 | 38844 | |||
| Optical Data | ||||||
| Gloss (45⁰) | Gardner | D-2457 | >94 | |||
| Haze | % | D-1003 | 1.5-2.0 | |||
| Mechanical Data | ||||||
| Tensile Strength | MD | kg/cm² | D-882 | 1300-1600 | ||
| TD | 2800-3300 | |||||
| Elongation | MD | % | D-882 | 140-190 | ||
| TD | 40-80 | |||||
| Thermal Data | ||||||
| Shrinkage (120⁰C/248 ⁰F,5 min) | MD | % | D-1204 | 3.0-5.0 | ||
| TD | 0.5-2.5 | |||||
| Barrier Data | ||||||
| MVTR (38⁰C, 90% RH) | g/m²/day | F-1249 | <7.0 | <6.5 | <6.5 | |
| MVTR (100 °F,90%RH) | g/100 in²/day | F-1249 | <0.45 | <0.41 | <0.41 | |
| CTM : Cosmo Test Method | MD : Machine Direction | TD : Transverse Direction | UT: Un-treated |
| Disclaimer : The information provided above is based on COSMO FILMS LTD's conclusive tests, which are indicative only and provided as guidelines.They do not constitute a guarantee of any specific product attributes or the suitability of products for specific applications | |||
| Storage condition : Storage temperature to be maintained 25 Deg.C (+/-5 Deg C) & relative humidity 55% (+/-5%) to avoid accelerated reduction of surface treatment level. | |||
Updation Date : 2025-Oct-10