Plain Printing & Lamination Film
PCT-2 (NT) HR
Structure
Treated, modified OPP layer
Additive modified OPP core
Treated, printable OPP layer
Description
It is a co-extruded, both side treated and out side modified Biaxially Oriented Polypropylene film
Features
- Excellent printability at high speed
- High heat resistance (up to 160°C*)
- Good ink adhesion
- Good antistatic
- Improved puncture resistance
Applications
- Used as a reverse printed top layer into multilayer laminate
Typical values
| Properties | Ref. | Units | ASTM#/ Test Method | PCT-2 (NT) HR |
|---|
| Physical Data | |||||
| Average Thickness | Micron | D-374-C | 15 | 18 | |
| Gauge | 60 | 72 | |||
| Mils | 0.6 | 0.7 | |||
| Thickness Variation | %(±) | 3 | |||
| Density | g/cc | 0.905 | |||
| Average substance | g/m² | 13.5 | 16.3 | ||
| Kinetic COF | NPS-NPS | D-1894 | < 0.35 | ||
| Yield | m²/Kg | D-4321 | 73.7 | 61.3 | |
| in²/lb | 51786 | 43098 | |||
| Optical Data | |||||
| Gloss (45⁰) | Gardner | D-2457 | > 90 | ||
| Haze | % | D-1003 | 3.0 - 3.5 | ||
| Mechanical Data | |||||
| Tensile Strength | MD | kg/cm² | D-882 | 1300 -1600 | |
| TD | 2800 -3300 | ||||
| Elongation | MD | % | D-882 | 140 -190 | |
| TD | 40 -80 | ||||
| Thermal Data | |||||
| Shrinkage (120⁰C/248 ⁰F,5 min) | MD | % | D-1204 | 3.0 - 5.0 | |
| TD | 0.5 - 2.5 | ||||
| Barrier Data | |||||
| MVTR (38⁰C, 90% RH) | g/m²/day | < 7.0 | < 6.5 | ||
| CTM : Cosmo Test Method | MD : Machine Direction | TD : Transverse Direction | NPS: Non Printable Side | HR : Heat Resistance |
| Disclaimer : The information provided above is based on COSMO FILMS LTD's conclusive tests, which are indicative only and provided as guidelines.They do not constitute a guarantee of any specific product attributes or the suitability of products for specific applications | ||||
| Storage condition : Storage temperature to be maintained 25 Deg.C (+/-5 Deg C) & relative humidity 55% (+/-5%) to avoid accelerated reduction of surface treatment level. | ||||
| Note : NPS side is HR side | ||||