High speed print Lamination
PCT-2(P/L) OL
Structure
Treated OPP layer
Additive Modified OPP core
Treated OPP Layer
Description
It is a co-extruded,plain and both sides treated Bi-axially Oriented Polypropylene film
Features
- Good Antistatic
- Excellent machinability
- Low Haze
Applications
- High gloss lamiantion with printed and un-printed paper and paper board
- For cartoon lamination
Typical values
| Properties | Ref. | Units | ASTM#/ Test Method | PCT-2(P/L) OL |
|---|
| Physical Data | ||||
| Average Thickness | Micron | D-374-C | 15 | |
| Gauge | 60 | |||
| Mils | 0.6 | |||
| Thickness Variation | %(±) | 3 | ||
| Density | g/cc | 0.905 | ||
| Average substance | g/m² | 13.6 | ||
| Surface Tension(min) | Both Side | dynes/cm | D-2578 | 38 |
| Kinetic COF | F-F | D-1894 | 0.20-0.35 | |
| Yield | m²/Kg | D-4321 | 73.5 | |
| in²/lb | 51675 | |||
| Optical Data | ||||
| Gloss (45⁰) | Gardner | D-2457 | >93 | |
| Haze | % | D-1003 | 1.4-2.0 | |
| Mechanical Data | ||||
| Tensile Strength | MD | kg/cm² | D-882 | 1100-1500 |
| TD | 2400-2800 | |||
| Elongation | MD | % | D-882 | 130-180 |
| TD | 30-80 | |||
| Thermal Data | ||||
| Shrinkage (120⁰C/248 ⁰F,5 min) | MD | % | D-1204 | 3.0-5.0 |
| TD | 1.0-3.0 | |||
| CTM : Cosmo Test Method | MD : Machine Direction | TD : Transverse Direction | F : Film |
| Disclaimer : The information provided above is based on COSMO FILMS LTD's conclusive tests, which are indicative only and provided as guidelines.They do not constitute a guarantee of any specific product attributes or the suitability of products for specific applications | |||
| Storage condition : Storage temperature to be maintained 25 Deg.C (+/-5 Deg C) & relative humidity 55% (+/-5%) to avoid accelerated reduction of surface treatment level. | |||
Updation Date : 2025-Sep-22