Pressure Sensitive Label Facestock Film Transparent, Non Coated
PP (Premere) LBS
Structure
Print receptive polyolefin layer
Transparent PP core layer
Untreated layer
Description
It is a co-extruded, one side print skin and other side untreated polypropylene film.This film is specifically designed for better printing and adhesive anchorage.
Features
- Good runability for converting and die cutting process
- Suitable for printing on UV Flexographic machines at high speed
- Good ink adhesion
- Ideal for labeling products with special contours requiring good conformability
Applications
- Pressure Sensitive Labels
Typical values
| Properties | Ref. | Units | ASTM#/ Test Method | PP (Premere) LBS |
|---|
| Physical Data | |||||
| Average Thickness | Micron | D-374-C | 50 | 70 | |
| Gauge | 200 | 280 | |||
| Mils | 1.96 | 2.80 | |||
| Average substance | g/m² | 45.2 | 63.3 | ||
| Surface Tension(min) | dynes/cm | D-2578 | 38 | ||
| Kinetic COF | UT-UT | D-1894 | 0.40-0.50 | ||
| Yield | m²/Kg | D-4321 | 22.12 | 15.8 | |
| in²/lb | 15551 | 11107 | |||
| Optical Data | |||||
| Haze | % | D-1003 | <6 | ||
| Mechanical Data | |||||
| Tensile Strength | MD | kg/cm² | D-882 | 300-500 | |
| TD | 200-300 | ||||
| Elongation | MD | % | D-882 | >579 | |
| TD | >579 | ||||
| Tear Strength | MD | g | Elmendorf | 40 | |
| TD | 120 | ||||
| CTM : Cosmo Test Method | MD : Machine Direction | TD : Transverse Direction | UT : Un-treated |
| Disclaimer : The information provided above is based on COSMO FILMS LTD's conclusive tests, which are indicative only and provided as guidelines.They do not constitute a guarantee of any specific product attributes or the suitability of products for specific applications | |||
| Storage condition : Storage temperature to be maintained 25 Deg.C (+/-5 Deg C) & relative humidity 55% (+/-5%) to avoid accelerated reduction of surface treatment level. | |||
| Note : It is recommended to provide corona treatment on untreated side before printing. | |||
Updation Date : 2025-Sep-22